Description
Description
- Innovative material, grade 23 titanium
- Highly biocompatible
- Low specific weight
- Optimal modulus of compatibility for a more stable result
Composition in %
Titanium (Ti) 90 % Aluminium (Al) 6 % Vanadium (V) 4 % Others Fe
Physical and mechanical features
| Solidus-liquidus temperature |
1605 ÷ 1660 °C |
| Melting point |
1710 °C |
| Density |
4,426 g/cmc |
| Vickers hardness |
312 HV10 |
| Percentage elongation at fracture |
14 % |
| Yield load strength (Rp0.2) |
(Rp0.2) 880 MPa |
| Modulus of elasticity |
114 GPa |
| Colour |
White |
CE 0425 MATERIAL ACCORDING TO: ASTM F136 Dimensions PLAIN Ø98.5x10mm | DISC CUT Ø98.5x12mm | DISC CUT Ø98.5×13.5mm | DISC CUT Ø98.5x14mm | DISC CUT Ø98.5x15mm | DISC CUT Ø98.5x16mm | DISC CUT Ø98.5x18mm | DISC CUT Ø98.5x20mm | DISC CUT Ø98.5x22mm | DISC CUT Ø98.5×24.5mm | DISC CUT Ø98.5x25mm